Method of marking or lettering metallic components

ABSTRACT

A method for marking or lettering metallic components, specifically those consisting of titanium and titanium alloys, characterized by the steps of:  
     covering the area requiring lettering or marking with a writing ink or writing gel  
     marking or lettering the area by means of a laser scanner.

[0001] This invention relates to a method for marking or lettering metallic components, specifically those consisting of titanium or titanium alloys according to claim 1.

[0002] It is known to letter or mark metallic components using lasers. For example, this is accomplished by means of a mask which contains the lettering or marking. However, it is also possible to apply a marking or lettering directly by appropriately sweeping a laser beam. As a result, a thermal deformation takes place in the microstructure of the metallic component in the area close to the surface. Although such a marking is permanent it possibly has an adverse effect with regard to the strength of the metallic component.

[0003] Further, it is known to apply a paste to a metallic component and to treat it thermally using a laser light in order that a fixed union be established between the paste which is applied and the metallic component. The disadvantages are the expenditure that the known method involves and the fact that it is possible to remove such a lettering or marking.

[0004] It is the object of the invention to mark or letter a metallic component, specifically one made of titanium or a titanium alloy in which a permanent lettering or marking is performed with the surface of the metallic component not being attacked in a detrimental fashion.

[0005] The object is achieved by the features of patent claim 1.

[0006] In the invention, a writing ink or writing gel is applied to the area which requires marking or lettering. Such writing or marking inks are used in very varied writing utensils, for example and, amongst other things, are employed to mark metallic components. After its application, it is readily possible to remove the ink which was applied and has dried. In the inventive method, lettering is done by means of a laser scanner subsequent to the application of the writing gel or writing ink. At this stage, a thermal diffusion process takes place which causes particles or molecules of the writing gel or writing ink, within the area hit by the laser beam, to penetrate into the area close to the surface, but still to remain readily visible. It will then be no longer possible to remove the lettering or marking without removing metallic material. Then, the writing ink or the like which is outside the lettering or marking may be readily removed with a suitable agent, e.g. a solvent or the like.

[0007] Most writing inks contain graphite in a finely dispersed distribution. The effect described can be observed in liquids of this type. Obviously, a carbonization occurs in the metal, specifically in titanium or titanium alloys.

[0008] The invention allows to use a laser scanner for marking metallic components without causing them to be harmed in any way in their structure or strength. The further advantage of the inventive method is that the laser beam does not need to be so rich in energy as it does when metallic components of the prior art are engraved.

[0009] The inventive method is suited for use with all workpieces consisting of metal, but specifically with those consisting of titanium and titanium alloys. 

1. A method for marking or lettering metallic components, specifically those consisting of titanium and titanium alloys, wherein a substance is supplied to an area requiring lettering or marking and said area is marked or lettered by means of a laser scanner, characterized in that a writing ink or writing gel containing graphite in a dispersed form is applied to the area requiring lettering or marking and the action of the laser beam causes the metal to undergo carbonization. 